Ábhair choitianta cruach dhosmálta ：
CHINA GB | SAM AISI | RA BS | AN FHRAINC NF | AN GHEARMÁIN DIN | JAPAN JIS |
1Cr13 | 410 | 410S21 | Z12C13 | X10Cr13 (1.4006) | SUS410 |
2Cr13 | 420 | 420S37 | Z20C13 | X20Cr13 (1.4021) | SUS420J1 |
1Cr17Ni2 | 431 | 431S29 | / | X22CrNi17 (1.4057) | SUS431 |
0Cr18Ni9 | 304 | 304S15 | Z6CN18-09 | X5CrNi18 9 (1.4301) | SUS304 |
/ | 316 | / | Z6CND17-12 | X2CrNiMo1810 (1.4401) | SUS316 |
00Cr18Ni10 | 304L | 304L12 | Z2CN18-10 | X2CrNi18 9 (1.4306) | SUS304L |
/ | 316L | 316S12 | Z2CND17-12 Z2CND17-13 | X2CrNiMo1810 (1.4404) X2CrNiMo1812 (1.4435) | SUS316L |
0Cr17Ni4Cu4Nb | 17-4PH | / | / | X5CrNiCuNb16-4 | SUS630 |
Is ábhar coitianta cruach dhosmálta é an SS304, ar a dtugtar freisin cruach dhosmálta 18-8 le cruas ard agus teocht ard resistant 800 ℃ sa tionscal, a úsáidtear go forleathan sa tionscal maisiúcháin tionscail agus troscáin agus sa tionscal bia agus míochaine.
Is cineál cruach dhosmálta ildánach é an 304 a úsáidtear go forleathan chun trealamh agus comhpháirteanna a dhéanamh a éilíonn feidhmíocht chuimsitheach mhaith (friotaíocht creimeadh agus múnlú). Chun an fhriotaíocht creimeadh is gné dhílis de chruach dhosmálta a choinneáil, caithfidh níos mó ná 18% cróimiam agus níos mó a bheith sa chruach. ná 8% ábhar nicil. Déantar an 304 Cruach Dhosmálta de réir chaighdeáin ASTM na SA
Cruach dhosmálta 304 Comhdhéanamh ceimiceach ：
C: ≤0.08
Si: ≤1.00
Mn: ≤2.00
P: ≤0.045
S: ≤0.030
Cr: 18.0-20.0
Ni: 8.00-10.5
Cruach dhosmálta 304 maoin fhisiceach ：
Neart teanntachta: σb≥515-1035MPa
Neart Toradh: σ0.2≥205MPa
In-fhairsingeacht: δ5 ≥40%
Laghdú an achair: ψ (%) ≥?
Cruas ： ≤201HBW; ≤92HRB; ≤210HV
Dlús: 7.93 g / cm³ （20 ℃）
Leáphointe ： 1398 ~ 1454 ℃
toilleadh teasa sonrach ： 0.50 KJ / kg * K （0 ~ 100 ℃）
seoltacht theirmeach ： 16.3 W / m * K （100 ℃） ， 21.5 W / m * K （500 ℃）
Leathnú Líneach ： 17.2 （10-6/K）（0~100℃），18.4（10-6/K）（0~500℃）
Friotaíocht Leictreach ： 0.73X10-6Ω·m2/m（20℃）
Modulus Leaisteacha Fadaimseartha ： 193 KN / mm2（20℃）